1. The A and B agents should be taken according to the weight ratio and mixed thoroughly to avoid not being cured completely.
2. Agent B should be sealed in time to avoid moisture absorption.
3. Operational time: refers to the time for 100g mixing under the condition of 25℃.
4. The above reaction is an exothermic reaction, so pay more attention to below features:
1) The more the configuration amount, the faster the curing reaction speed.
2) The higher the ambient temperature, the faster the curing reaction speed.on the contrary, the lower the ambient temperature, the slower the curing speed.
3) To achieve better performance, it must be formulated in strict accordance with the specified ratio.
Specification:
| Items | Units/conditions | Technical Data |
| Viscosity | Shore-D | 80-85 |
| Volume resistivity | 25℃/ Ω./ cm | 4.3x1015 |
| Surface resistivity | 25℃/ Ω. | 2.6x1014 |
| Dielectric strength | 25℃ KV/MM | 25 |
| Coefficient of linear expansion | CM/K | <6.1x10-5 |
| Glass transition temperature | ℃ | >90 |
| Temperature resistant | ℃ | -60~120 |
The above performance data is typical data measured in a laboratory environment
with a temperature of 25°C and a humidity of 70%. It is for customer reference only
Product Paramenters
Below relevant product data and descriptions provided in this document are based on a specific environment Under test or our current knowledge and experience. The actual application of products is affected by artificial or natural factors such as substrates, processes, equipment, environment, storage, transportation, user experience, etc.
Tips:
1. If it is used to contact food after curing, the temperature of the food should not exceed 50 degrees Celsius.
2. When the hardness is higher than 82D (Shaw hardness), it can be directly polished.
3. The mixing quantity should not exceed 5kg, and the casting thickness should not exceed 3cm each layer.
4. When the temperature is higher than 25 degrees Celsius, it will cure faster, please reduce the number of mixing/casting by half, or it will be hardened in the container;
5.Curing time will be depend on room temperature and casting thickness , the room temperature higher it is, the faster curing it does. The thinner it cast the longer curing time it needs;
How to Choose Product Model:
Aorun epoxy resin is suitable for machinery, petrochemical, vehicle, electronic products, electrical equipment, construction, decoration, special purpose and other industries, especially for special purpose and multiple purposes.
Packaging:
We offer different size of packaging, 5kg buckets and 20kg buckets are normal size. Customized